Multifunctional Poly(Acrylic Acid)-Coated EuBiGdO Nanocomposite as an Effective Contrast Agent in Spectral Photon Counting CT, MRI, and Fluorescence Imaging.
Int J Nanomedicine 20:4759-4775
Authors: Yusuf O Ibrahim, Nabil Maalej, Aamir Younis Raja, Ahsanulhaq Qurashi, Mohamed Rahmani, Thenmozhi Venkatachalam, Osama Abdullah, Haidee J Paterson, Gobind Das, Curtis C Bradley, Rasha A Nasser, Charalampos Pitsalidis
Affiliations
- Department of Physics, Khalifa University of Science and Technology, Abu Dhabi, 127788, United Arab Emirates. Functional Biomaterials Group, Khalifa University of Science and Technology, Abu Dhabi, 127788, United Arab Emirates.
- Department of Physics, Khalifa University of Science and Technology, Abu Dhabi, 127788, United Arab Emirates.
- Functional Biomaterials Group, Khalifa University of Science and Technology, Abu Dhabi, 127788, United Arab Emirates.
- Department of Chemistry, Khalifa University of Science and Technology, Abu Dhabi, 127788, United Arab Emirates.
- Department of Biological Sciences, College of Medicine & Health Sciences, Khalifa University, Abu Dhabi, 127788, United Arab Emirates.
- Center for Biotechnology, Khalifa University, Abu Dhabi, 127788, United Arab Emirates.
- Core Technology Platform Operations, New York University Abu Dhabi, Abu Dhabi, 129188, United Arab Emirates.
- Department of Biomedical Engineering and Biotechnology, Khalifa University of Science and Technology, Abu Dhabi, 127788, United Arab Emirates.
- Advanced Research and Innovation Center (ARIC) Khalifa University, Abu Dhabi, 127788, United Arab Emirates.
Abstract
Introduction
Recently, diagnostic methods based on multimodal and non-invasive imaging, such as MRI and CT scanners, have been developed for accurate cancer diagnosis. A key limitation of these imaging systems is their low contrast. Therefore, developing stable, non-toxic, and efficient multimodal imaging contrast agents is desirable. In this work, we demonstrated the synthesis of a poly(acrylic acid) (PAA) - coated nanoparticles (NPs), PAA@EuBiGdO-NPs as an imaging agent for contrast enhancement in spectral photon-counting computed tomography (SPCCT), magnetic resonance imaging (MRI) and fluorescence imaging (FL).
Methods
We synthesized PAA-coated EuBiGdO-NPs using a polyol method by dissolving metal nitrates and PAA in triethylene glycol. NaOH solution was added under constant heating at 180°C. The nanoparticles were precipitated with the addition of ethanol, then washed, dried, calcined at 600°C, and redispersed in water for further studies. The nanoparticles were characterized using TEM, SEM, XRD, XPS, FTIR, and PL spectroscopy. PAA@EuBiGdO-NPs were tested in vitro for their cytocompatibility with lung cancer epithelial cells (A549). The nanocomposite image contrast enhancement was evaluated using SPCCT, MRI, and FL imaging.
Results
The cell viability study showed that PAA@EuBiGdO-NPs is safe up to 250 µg/mL, exhibiting IC50 values of 365.8 and 337.8 µg/mL after 24 and 48 hours, respectively. The NPs have strong X-ray attenuation with a slope of ~61 HUmL/mg, as determined from the SPCCT concentration-dependent analysis. The MRI of the NPs reveals a high T1 contrast with a relaxivity of 11.77 mMs. Fluorescence imaging of cells incubated with PAA@EuBiGdO₃-NPs shows strong red luminescence.
Conclusion
The new nanocomposite has proven to be an effective trimodal contrast agent with high attenuation in CT, enhanced T1 signal in MRI, and strong red luminescence in FL imaging with promising diagnostic capabilities.
MeSH
Cells, Contrast Media, Nanomedicine, Nanoparticles, Neoplasms, Magnetic Resonance Imaging, Multimodal Imaging, Multifunctional Nanoparticles, Nanocomposites